LNP™ THERMOCOMP™ XF006S compound
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Hz16O5_LNP-THERMOCOMP-XF006S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP XF006S is a compound based on Amorphous Nylon containing 30% Glass Fiber. Added feature of th is grade is: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound XF-1006 HS Product reorder name: XF006S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 7.0E-3 to 9.0E-3 | % | |
| Across Flow : 24 hr | 0.20 to 0.40 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.22 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.28 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9660 | MPa | ASTM D638 |
| -- | 9030 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 138 | MPa | ASTM D638 |
| Break | 141 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.6 | % | ASTM D638 |
| Break | 2.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 9060 | MPa | ASTM D790 |
| -- 5 | 8920 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 214 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 209 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 208 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 57 | J/m | ASTM D256 |
| 23°C 8 | 5.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 630 | J/m | ASTM D4812 |
| 23°C 9 | 38 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 11.5 | J | ASTM D3763 |
| -- | 3.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 142 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 144 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 138 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 137 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 4.4E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 3.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 6.0 to 12 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 290 to 300 | °C | |
| Processing (Melt) Temp | 260 to 300 | °C | |
| Mold Temperature | 50.0 to 100 | °C | |
| Back Pressure | 0.170 to 0.340 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecnoflon® TN 50A | Solvay Specialty Polymers | Fluorelastomer | Tecnoflon® |
| Yuyao PP TL303 | Yuyao Tenglong Plastics Co., Ltd. | PP, Unspecified | Yuyao PP |
| Chiao Fu PA66 MD212LB30 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| Hostacom TRC 152N | LyondellBasell Industries | PP Alloy | Hostacom |
| Axiall PVC 3533 | Axiall Corporation | PVC, Rigid | Axiall PVC |