TOTAL Polyethylene Lumicene® M 1811 PCE
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HynWtW_TOTAL-Polyethylene-Lumicene-M-1811-PCE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lumicene® mPE M1811 PCE is a metallocene based Linear Low Density Polyethylene with hexene as comonomer. This product contains slip and anti-block agents. Lumicene® mPE M1811 PCE can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control in comparison with conventional LLDPE and other metallocene based polyethylene. Lumicene® mPE M1811 PCE is especially dedicated to film applications where excellent optical properties in combination with outstanding impact resistance (even at low temperature) and sealing strength are required, particularly in blend and coextrusion with LLDPE or LDPE. Lumicene® mPE M1811 PCE is suited for many applications in the field of consumer, industrial, food or hygiene packaging such as bags, deep freeze, stretch hood and lamination. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-3 | ||
| MD : Yield | 10.0 | MPa | ISO 527-3 |
| TD : Yield | 10.0 | MPa | ISO 527-3 |
| MD : Fracture | 68.0 | MPa | ISO 527-3 |
| TD : Fracture | 62.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture | 670 | % | ISO 527-3 |
| TD : Fracture | 700 | % | ISO 527-3 |
| Dart Drop Impact | > 1200 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 1000 µm | 110 | N | ISO 6383-2 |
| TD : 1000 µm | 170 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 105 | °C | ISO 306 |
| Melting Temperature | 111 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 75 | ASTM D2457 | |
| Haze | 5.5 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 230 | °C |
| Extrusion instructions |
|---|
| BUR: 1.5:1 to 4.5:1Die Gap: 0.8 to 2.8 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV 4755B42 | Teknor Apex Company | TPV | Sarlink® TPV |
| Staramide R1000HI620 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| EPO-TEK® 301-2FL | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| LEXAN™ LUX2910T_ resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Sylvin 83012-90UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |