RTP 132 HF
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HvxG5v_RTP-132-HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3450 | MPa | ASTM D638 |
| Tensile Strength | 30.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 2760 | MPa | ASTM D790 |
| Flexural Strength | 48.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 27 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 480 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 135 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 79.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, Values per RTP Company testing.) | HB | UL 94 |
| Additional Information |
|---|
| Molding Shrinkage, Linear-Flow, ASTM D955, 6.35mm: 15mm/m. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 218 - 274 | °C | |
| Middle Temperature | 218 - 274 | °C | |
| Front Temperature | 218 - 274 | °C | |
| Mold Temperature | 32.0 - 66.0 | °C | |
| Injection Pressure | 68.9 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYNIL® P125 | Nilit Plastics | Nylon 66 | POLYNIL® |
| Bynel® 3810 | DuPont Packaging & Industrial Polymers | EVA | Bynel® |
| Keyflex® BT 1040D | LG Chem Ltd. | TPC-ET | Keyflex® BT |
| Karina NATURAL PVC COMPOUND -E 900-25/ 1-AYR-IS-LF(*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plasmer 1050DB/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |