Latamid 66 H2 G/25-V0KB3
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HuHobN_Latamid-66-H2-G-25-V0KB3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on Polyamide 66 (PA 66). Heat stabilised. Glass fibres. UL94 V-0 classified, with red phosphorous. Product UL certified. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.0 to 1.2 | % | |
| Flow | 0.35 to 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| 23°C | 8200 | MPa | |
| 60°C | 6900 | MPa | |
| 90°C | 4200 | MPa | |
| 120°C | 3500 | MPa | |
| 150°C | 2700 | MPa | |
| Tensile Stress | ISO 527-2 | ||
| Yield, 90°C | 70.0 | MPa | |
| Yield, 120°C | 50.0 | MPa | |
| Yield, 150°C | 40.0 | MPa | |
| Break, 23°C | 135 | MPa | |
| Break, 60°C | 100 | MPa | |
| Break, 90°C | 65.0 | MPa | |
| Break, 120°C | 50.0 | MPa | |
| Break, 150°C | 40.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield, 90°C | 3.7 | % | |
| Yield, 120°C | 3.8 | % | |
| Yield, 150°C | 4.1 | % | |
| Break, 23°C | 2.2 | % | |
| Break, 60°C | 2.6 | % | |
| Break, 90°C | 4.2 | % | |
| Break, 120°C | 4.2 | % | |
| Break, 150°C | 4.7 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 7.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 50 | kJ/m² | |
| 23°C | 60 | kJ/m² | |
| Notched Izod Impact (23°C) | 95 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 225 | °C | ISO 75-2/A |
| Continuous Use Temperature | 125 | °C | |
| Vicat Softening Temperature | 240 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 1.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Oxygen Index | 26 | % | ASTM D2863 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mold Shrinkage Pressure | 60.0 | MPa | ISO 294-4 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Injection Rate | Moderate |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 GB 20 TFE 20 | RTP Company | Acetal (POM) Copolymer | RTP |
| Sinvicomp SIF4569 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Sylvin 2900-68 Clear Green 3181 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| CALP 3514G | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Polifil® PP RMT-40V | The Plastics Group | PP, Unspecified | Polifil® PP |