LUBLENE GK30 NATURAL
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | LUBEN PLAST srl |
| Trademark: | LUBLENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Hu9Q1X_LUBLENE-GK30-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on PP first choice natural colour. With glass beads 30%. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 to 1.14 | g/cm³ | ISO 1183/A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 to 3000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/5 | ||
| Yield | 23.0 to 27.0 | MPa | |
| Break | 18.0 to 22.0 | MPa | |
| Tensile Strain | ISO 527-2/1A/5 | ||
| Yield | 4.0 to 5.0 | % | |
| Break | 25 to 30 | % | |
| Flexural Modulus 1 | 1500 to 2500 | MPa | ISO 178 |
| Flexural Stress 2 | 30.0 to 40.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 to 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 20 to 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 25 to 35 | J/m | ASTM D256A |
| 23°C 3 | 20 to 30 | kJ/m² | ASTM D256 |
| 23°C | 3.0 to 4.0 | kJ/m² | ISO 180/A |
| 23°C 4 | 2.5 to 3.5 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 20 to 30 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 120 to 130 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 125 to 135 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 60.0 to 70.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 100 to 110 | °C | ISO 306/A120 |
| -- | 95.0 to 105 | °C | ISO 306/B120 |
| Melting Temperature | 165 to 170 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| 4 . | Notch A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Braskem PP C7057-07 (Injection Molding) | Braskem Europe GmbH | PP Impact Copolymer | Braskem PP |
| Ferro PP TPP40AC26NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| ICORENE® 1761 V2 White 1801 | ICO Polymers EMEA, A Division of A. Schulman | mMDPE | ICORENE® |
| IROGRAN® A 85 P 4380 | Huntsman Corporation | TPU-Polyether | IROGRAN® |
| SQUARE® LIM1500-30A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |