LUVOCOM®1-0889-4 is a polyamide 66 (nylon 66) material, which contains glass and carbon fiber reinforced materials. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 1-0889-4 are: flame retardant/rated flame Conductivity Electrostatic protection Good stiffness heat stabilizer Typical application areas include: textile/fiber engineering/industrial accessories Automotive Industry business/office supplies

General Information
Filler / Reinforcement	Glass, carbon fiber reinforced materials
Additive	heat stabilizer
Features	Conductivity Rigid, good Electrostatic discharge protection Good strength Thermal Stability
Uses	Textile applications Engineering accessories Application in Automobile Field Business equipment
Appearance	Black

Physical	Nominal Value	Unit	Test Method
Density	1.32	g/cm³	ISO 1183
Molding Shrinkage	0.20 - 0.50	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 1.0	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	12500	MPa	ISO 527-2
Tensile Stress (Break)	200	MPa	ISO 527-2
Tensile Strain (Yield)	3.0	%	ISO 527-2
Flexural Modulus	10500	MPa	ISO 178
Flexural Stress	290	MPa	ISO 178
Coefficient of Friction
Dynamic	0.31
Static	0.27
Flexural Strain at Flexural Strength	3.9	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	160	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance		ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	11	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	65	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	245	°C	ISO 75-2/A
Continuous Use Temperature	120	°C	UL 746B

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	< 1.0E+4	ohms	IEC 60093

Flammability	Nominal Value	Unit	Test Method
Flame Rating ¹	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature
Hot air dryer, A	75.0	°C
Vacuum dryer, B	105	°C
Drying Time
Hot air dryer, A	6.0 - 16	hr
Vacuum dryer, B	4.0 - 6.0	hr
Suggested Max Moisture	0.10	%
Rear Temperature	290 - 310	°C
Middle Temperature	290 - 310	°C
Front Temperature	290 - 310	°C
Nozzle Temperature	280 - 300	°C
Processing (Melt) Temp	290	°C
Mold Temperature	90.0 - 120	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. Due to rapid absorption of water, originally sealed containers should only be opened immediately prior to processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. Due to rapid absorption of water, originally sealed containers should only be opened immediately prior to processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Note Message
1 .	Not recognized by UL.

Category:	Nylon 66 , Polyamide 66
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Hu0Bkf_LUVOCOM-1-0889-4.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Zytel® 101 NC010	DuPont Performance Polymers	Nylon 66	Zytel®
Axiall PVC 5006 White	Axiall Corporation	PVC, Rigid	Axiall PVC
Ferro PE NPE00IA02NA	Ferro Corporation	PE, Unspecified	Ferro PE
Durethan® BKV 30 W1 000000	LANXESS GmbH	Nylon 6	Durethan®
Sumiliteresin® PR-217	SBHPP	Phenolic	Sumiliteresin®