Eraclene® DB 506
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Eraclene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ht11l2_Eraclene-DB-506.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eraclene DB 506 is a high density polyethylene resin (HDPE), hexene copolymer, obtained by gas phase technology process. The main properties of Eraclene DB 506 are emphasized when it is used for production of drip irrigation pipe. Main Application Eraclene DB 506 can be easily used in blend with LLDPE and LDPE grades to modify the final properties of the drip irrigation pipe accordging to the specific needs. For outdoor application, it is strongly suggested to add Anti UV. The combined usage of these additives together with Carbon Black can provide outstanding resistance to UV radiation. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.939 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.23 | g/10 min | |
| 190°C/5.0 kg | 0.90 | g/10 min | |
| Environmental Stress-Cracking Resistance (Compression Molded) | > 1000 | hr | ISO 22088 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 58 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield, Compression Molded | 18.0 | MPa | |
| Break, Compression Molded | 28.0 | MPa | |
| Tensile Strain (Break, Compression Molded) | > 800 | % | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 690 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 25.0 µm | 20.0 | kN/m | |
| TD : 25.0 µm | 170.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 119 | °C | ISO 306/A |
| Melting Temperature | 129 | °C | Internal Method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP2795 | LyondellBasell Industries | PP Random Copolymer | Moplen |
| TPC PVC SG730 | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| NEOPLAST 173 C | Zylog Plastalloys | TPV | NEOPLAST |
| Acrigel® ECL500 | Unigel Plásticos | Acrylic (PMMA) | Acrigel® |
| Sumiliteresin® PR-50641 | SBHPP | Phenolic | Sumiliteresin® |