POLYFORT® FPP 40 T LE K1846
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFORT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HsleEr_POLYFORT-FPP-40-T-LE-K1846.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% talc filled PP-Homopolymer; low emission; long term heat stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 14.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 89.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4200 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 30.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 3.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 16 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 120 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 79.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 154 | °C | ISO 306/A50 |
| -- | 93.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravamid® R200 T53 | Ravago Group | Nylon 6 | Ravamid® |
| Toyolac® 325 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| ISOTHANE® 1160D | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |
| OXPEKK® C | Oxford Performance Materials, Inc. | PEKK | OXPEKK® |
| Plexiglas® HFI7G | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |