Durez® 31906 (Compression)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | Durez® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HsVhHC_Durez-31906-Compression-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Durez 31906 Black Phenolic is a medium impact, molding compound. It is designed for applications where additional mechanical strength is required. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Apparent Density | 0.55 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D6289 |
| Water Absorption | 0.40 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8300 | MPa | ASTM D638 |
| Tensile Strength | 55.0 | MPa | ASTM D638 |
| Flexural Strength | 90.0 | MPa | ASTM D790 |
| Compressive Strength | 214 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 35 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 204 | °C | ASTM D648 |
| RTI Elec (3.00 mm) | 150 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| -- 1 | 13 | kV/mm | ASTM D149 |
| -- 2 | 11 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 6.00 | ASTM D2520 | |
| Dissipation Factor (1 MHz) | 0.060 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 | |
| 6.00 mm | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Shelf Life | 52 | wk |
| Additional Information |
|---|
| Test Specimens Molded at 340-350°FTypical transfer-molded shrinkage is 0.007 in/in |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| 2 . | Method B (step by step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 7510 GF 50 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| BMC 685 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| FRblend® PBT-1500 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PBT | FRblend® |
| Kepamid® 1330M7 | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |
| Axiall PVC 9175 | Axiall Corporation | PVC, Flexible | Axiall PVC |