LubriOne™ ATH-000/18T 2S
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ho1wZe_LubriOne-ATH-000-18T-2S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 2.0 to 2.3 | % | ASTM D955 |
| Water Absorption (24 hr, 3.18 mm) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2410 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 37.9 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.0 to 5.0 | % | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength | 37.9 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.25 | ||
| vs. Steel - Static | 0.14 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 53 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 124 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 116 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 193 to 216 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mineralblend® PP-2800 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PP Homopolymer | Mineralblend® |
| Spartech ABS CamAlloy/ABS | Spartech Plastics | ABS | Spartech |
| Celstran® PA66-GF40-01 | Celanese Corporation | Nylon 66 | Celstran® |
| Dow Corning® C6-135 | Dow Corning Corporation | Silicone | Dow Corning® |
| ESTOPLAST XU 330BB01 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |