Eraclene® FB 506
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Eraclene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HnOgGz_Eraclene-FB-506.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eraclene FB 506 is a high density polyethylene resin (HDPE), hexene copolymer, with antioxidants, suitable for blown film extrusion. Its broad molecular weight distribution and density successfully combine excellent performance at high extrusion rates with high films strength and sealability. Main Application Eraclene FB 506 can be processed either in blend and in coextrusion. It is possible to use it pure for high rigidity grocery sacks and shopping bags. Usage in blend and/or in coextrusion with LDPE and LLDPE is also recommended for high strength thermo-shrinkable film, as well as for hygienic packaging. The excellent balance between drawability and bubble stability makes Eraclene FB 506 the optimum choice for manufacturing of high quality thin films characterized by outstanding mechanical properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.939 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 20 | g/10 min | |
| 190°C/5.0 kg | 0.80 | g/10 min |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness - Recommended / Available | 10 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 25 µm, Blown Film | 400 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 500 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 25 µm, Blown Film | 50.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 50.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm, Blown Film | 500 | % | |
| TD : Break, 25 µm, Blown Film | 750 | % | |
| Dart Drop Impact 1(25 µm, Blown Film) | 120 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 25.0 µm | 15.0 | kN/m | |
| TD : 25.0 µm | 180.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 119 | °C | ISO 306/A |
| Melting Temperature | 129 | °C | Internal Method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadraflex™ ALE-80A | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| Complet® LCF40-PEI | PlastiComp, Inc. | PEI | Complet® |
| Generic PET - Glass Fiber | Generic | PET | Generic |
| ELASTOSIL® LR 6240 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Geon™ Vinyl Flexible B5546 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |