UBESTA 3020 GX9
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | UBE Engineering Plastics, S.A. |
| Trademark: | UBESTA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HlOh88_UBESTA-3020-GX9.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UBESTA 3020 GX9 is a glass fibre reinforced Polyamide 12 for injection moulding application. Typical application is quick connectors in fuel line systems. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (235°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.70 | % | ISO 294-4 |
| Flow direction | 0.20 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.40 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 103 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 6.0 | % | ISO 527-2 |
| Flexural Modulus | 4900 | MPa | ISO 178 |
| Flexural Stress | 125 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C, complete fracture | 11 | kJ/m² | ISO 179/1eA |
| 23°C, complete fracture | 19 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 176 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 159 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 178 | °C | ISO 3146 |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Additional Information |
|---|
| The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.Abrasion Loss, ISO 9352, CS-17, 1000 rev.: 12 mg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zhongfa PP GR-30+ | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| Network Polymers PP PPR 20 3401 CAS | Network Polymers, Inc. | PP Random Copolymer | Network Polymers PP |
| LNP™ THERMOCOMP™ RF006EUC compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| MAJORIS FFR091 | AD majoris | PP, Unspecified | MAJORIS |
| TABOREN® PC 22 G 15 | SILON s.r.o. | PP Random Copolymer | TABOREN® |