RAMOFIN PPC364I6
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMOFIN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HkimsA_RAMOFIN-PPC364I6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% MINERAL AND GLASS-FIBER REINFORCED, HEAT RESISTANT POLYPROPYLENE FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.30 to 0.50 | % | |
| -- | 0.30 to 0.50 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5200 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 60.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 3600 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 90.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D256 |
| 23°C | 12 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 142 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 127 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 165 | °C | ISO 11357-3, ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 to 220 | °C | |
| Middle Temperature | 200 to 225 | °C | |
| Front Temperature | 205 to 230 | °C | |
| Mold Temperature | 30.0 to 65.0 | °C | |
| Injection Pressure | 70.0 to 105 | MPa | |
| Holding Pressure | 35.0 to 70.0 | MPa | |
| Back Pressure | 0.350 to 0.700 | MPa | |
| Screw Speed | 60 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMILITE® CEL-4560 | Sumitomo Bakelite Co., Ltd. | LLDPE | SUMILITE® |
| Sylvin 9812-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VESTOLIT® E 7031 | VESTOLIT GmbH & Co. KG | PVC Homopolymer | VESTOLIT® |
| CELLOMER® 2100D | Microcell Composite Company | SBS | CELLOMER® |
| Durolon® V2600 | Unigel Plásticos | PC | Durolon® |