Celstran® PP-GF20-02 Black
| Category: | PP Homopolymer , Polypropylene |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Hilexb_Celstran-PP-GF20-02-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celstran PP-GF20-02 is a 20% long glass fiber Polypropylene. This material imparts excellent impact and modulus properties that exceed that short fiber polyproylene. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 3.0E-3 | % | ASTM D955 |
| Transverse flow | 4.0E-3 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 89.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.4 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 4900 | MPa | ISO 178 |
| Flexural Stress (23°C) | 143 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 157 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 220 - 230 | °C | |
| Middle Temperature | 230 - 240 | °C | |
| Front Temperature | 240 - 250 | °C | |
| Nozzle Temperature | 240 - 250 | °C | |
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 30.0 - 70.0 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Feed Temperature: 20 to 50°CZone 4 Temperature: 250°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) M/HI-W | A. Schulman Europe | ABS | POLYMAN® |
| Miraprene® QS2208 | Mitsubishi Chemical Corporation | TPO (POE) | Miraprene® |
| Nylene® 5213 HS | Custom Resins Group | Nylon 6 | Nylene® |
| ASTALOY™ PC/ABS KMB | Marplex Australia Pty. Ltd. | PC+ABS | ASTALOY™ |
| SQUARE® SSR3918-70 | Shenzhen SQUARE Silicone Co., Ltd. | Silicone | SQUARE® |