LG ABS PI641
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HhzOvq_LG-ABS-PI641.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LG ABS PI641 is an acrylonitrile butadiene styrene (ABS) material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is extrusion. The main characteristics of LG ABS PI641 are: impact resistance. The typical application fields of LG ABS PI641 are: engineering/industrial accessories |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 | g/cm³ | ASTM D792 |
| -- | 1060 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Melt volume-flow rate (220°C/10.0 kg) | 7.60 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.70 | % | ASTM D955 |
| Water Absorption (Saturation) | 0.22 | % | ISO 62 3 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2 4 |
| Tensile Strength | |||
| Yield, 3.20mm 5 | 45.1 | MPa | ASTM D638 |
| Yield | 44.0 | MPa | ISO 527-2 6 |
| Tensile Elongation | |||
| Yield, 3.20mm 7 | > 5.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2 8 |
| Fracture, 3.20mm 9 | 20 | % | ASTM D638 |
| Tensile Elongation at Break | 14 | % | ISO 527-2 10 |
| Flexural Modulus 11(3.20 mm) | 2300 | MPa | ASTM D790 |
| Flexural Strength 12(3.20 mm) | 68.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA 13 | ||
| -30°C | 39.6 | kJ/m² | ISO 179/1eA |
| 23°C | 56.5 | kJ/m² | ISO 179/1eA |
| Charpy impact strength | ISO 179/1eU 14 | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 440 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 410 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 9.40mm | 91.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 634 mm | 86.0 | °C | ASTM D648 |
| Glass Transition Temperature 15 | 110 | °C | ISO 11357-2 16 |
| Vicat Softening Temperature | |||
| -- | 94.0 | °C | ASTM D1525 17 |
| 50°C/h, B (50N) | 93.4 | °C | ISO 306 18 |
| Linear expansion coefficient | ISO 11359-2 19 | ||
| Flow | 9.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.3E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 20 |
| Volume Resistivity | > 1.0E+13 | ohms·m | IEC 60093 21 |
| Relative Permittivity (1 MHz) | 2.90 | IEC 60250 22 | |
| Dissipation Factor (1 MHz) | 0.013 | IEC 60250 23 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Behav. at thickness h (3.20 mm, UL) | HB | ISO 1210 24 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 180 - 210 | °C | |
| Cylinder Zone 2 Temp. | 190 - 230 | °C | |
| Cylinder Zone 3 Temp. | 200 - 250 | °C | |
| Cylinder Zone 4 Temp. | 200 - 250 | °C | |
| Adapter Temperature | 200 - 250 | °C | |
| Melt Temperature | 200 - 250 | °C | |
| Die Temperature | 200 - 250 | °C |
| Extrusion instructions |
|---|
| Minimum Moisture Content: 0.01%Roll Stack Temperature, Top: 70 to 100°CRoll Stack Temperature, Middle: 70 to 90°CRoll Stack Temperature, Bottom: 60 to 90°C |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | 50 mm/min |
| 6 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 7 . | 50 mm/min |
| 8 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 9 . | 50 mm/min |
| 10 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 11 . | 15 mm/min |
| 12 . | 15 mm/min |
| 13 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 14 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 15 . | 10 °C/min |
| 16 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 17 . | 速率 A (50°C/h), 载荷2 (50N) |
| 18 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 19 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 20 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 21 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 22 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 23 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 24 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E595 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Beetle® PBTC115F | Teknor Apex Company (Chem Polymer) | PBT+PET | Beetle® |
| Europrene® N 3330 | Versalis S.p.A. | NBR | Europrene® |
| ENFLEX VU-420-60A | Ravago Group | PP+EPDM | ENFLEX |
| LEXAN™ FXE4271L resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |