LNP™ LUBRICOMP™ RX85514 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Hhcemc_LNPLUBRICOMPRX85514compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RX85514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound PDX-R-85514 Product reorder name: RX85514 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792, ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture | 83.4 | MPa | ASTM D638 |
| Fracture | 78.0 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3810 | MPa | ASTM D790 |
| -- | 3570 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D256 |
| -40°C 1 | 3.8 | kJ/m² | ISO 180/1A |
| 23°C 2 | 4.8 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 64.0mm span 3 | 158 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 131 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 140 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 3478-NAT000 | Colorite Polymers | PVC, Rigid | Unichem |
| Chiao Fu PA6 MC312G50 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 6 | Chiao Fu PA6 |
| LNP™ LUBRILOY™ R2000 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |
| Plenco 02571 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |
| Hostaform® C 27021 XAP C | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |