PLUSTEK PA309G6
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | PLUSTEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HgpNZo_PLUSTEK-PA309G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% GLASS FIBER REINFORCED, UV STABILIZED POLYAMIDE 66.6 COPOLYMER FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.30 to 0.70 | % | ASTM D955 |
| -- | 0.30 to 0.70 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 5.6 | % | ASTM D570 |
| Saturation, 23°C | 5.6 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.7 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 190 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 9000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 280 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D256 |
| 23°C | 15 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 260 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | °C | ASTM D648, ISO 75-2/A |
| Maximum Use Temperature - Short Peaks Operation | 240 | °C | |
| Maximum Continuous Use Temperature | 130 | °C | |
| Melting Temperature | 256 | °C | ISO 11357-3, ASTM D3417 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength | 90 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.50 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Edgetek™ AT-25GB/000 NATURAL | PolyOne Corporation | Acetal (POM) Copolymer | Edgetek™ |
| Generic PUR-Ester | Generic | PUR-Ester | Generic |
| Hifax TKC 407P | LyondellBasell Industries | PP Copolymer | Hifax |
| OLEFISTA™ QM4301D/QMC292 | Mitsubishi Chemical Performance Polymers, Inc. | Elastomer, Specialty | OLEFISTA™ |
| Plenco 06527 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |