Infino LS-3104G
| Category: | PC , Polycarbonate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Hgnugt_Infino-LS-3104G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High-impact resistant PC/GF material with 10% GF reinforcement for LCD BLF |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 30 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.36 to 0.44 | % | |
| Across Flow : 3.20 mm | 0.33 to 0.40 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3300 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield 2 | 78.0 | MPa | ASTM D638 |
| Yield | 80.0 | MPa | ISO 527-2/50 |
| Break 3 | 77.0 | MPa | ASTM D638 |
| Tensile Elongation 4(Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | |||
| -- 5 | 3700 | MPa | ASTM D790 |
| -- 6 | 3800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 140 | MPa | ASTM D790 |
| -- 8 | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.18 mm | 79 | J/m | |
| 23°C, 6.35 mm | 59 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 135 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 135 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 120 | °C | |
| Desiccant Dryer | 120 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 240 to 250 | °C | |
| Middle Temperature | 260 to 270 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Nozzle Temperature | 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Pressure | 68.6 to 226 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SPESIN® KP212G30V0BL | Kolon Plastics, Inc. | PBT | SPESIN® |
| Wellamid® MR409 22H-NBK4 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| TRISTAR® PC-10R-(V6) | Polymer Technology and Services, LLC | PC | TRISTAR® |
| WELLAMID Nylon 6000 GVZ 45 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Nycast XHA | Cast Nylons Ltd. | Nylon 6 | Nycast |