Durethan® BKV 15 DUS008 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HgRhNs_DurethanBKV15DUS008000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 15 % glass fibers, injection molding |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.23 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.59 | -- | % | ISO 294-4 |
| Vertical flow direction : 120°C, 2 hours, 2.00mm 2 | 0.16 | -- | % | ISO 294-4 |
| Flow direction : 280°C, 2.00mm 3 | 0.35 | -- | % | ISO 294-4 |
| Flow direction : 120°C, 2 hours, 2.00mm 4 | 0.13 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6500 | 3100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 130 | 65.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | 12 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 5500 | 3100 | MPa | ISO 178/A |
| Flexural Stress 6 | ||||
| 3.5% strain | 180 | 80.0 | MPa | ISO 178/A |
| 23°C | 205 | 110 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 5.3 | 8.0 | % |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GR, 14-060, GF15 | -- | ISO 1874 |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Film Puncture Force 8 | 940 | -- | N | ISO 6603-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 45 | 45 | kJ/m² | ISO 179/1eU |
| 23°C | 50 | 100 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | < 10 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 40 | 40 | kJ/m² | ISO 180/1U |
| 23°C | 45 | 85 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 195 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 210 | -- | °C | ISO 306/B120 |
| Melting Temperature 9 | 220 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 260 - 290 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | 23°C |
| 9 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ LUB4343 | Mando Advanced Materials Co., Ltd. | PPS | SEPAZ™ |
| Tecodur® PB70 GR15 BK002 XA21 | Eurotec Engineering Plastics | PBT+PET | Tecodur® |
| Sinvicomp SBB4710 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Beetle® PBTB130F | Teknor Apex Company (Chem Polymer) | PBT+PET | Beetle® |
| LEXAN™ 3412HF resin | SABIC Innovative Plastics | PC | LEXAN™ |