Capilene® T 12 EV
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Carmel Olefins Ltd. |
| Trademark: | Capilene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HeUlQl_Capilene-T-12-EV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CAPILENE ® T 12 EV is a polypropylene homopolymer with narrow molecular weight distribution intended for spunbonded nonwovens. CAPILENE ® T 12 EV features: controlled rheology, anti-gasfading stabilisation, easy processability, high flow and optimal product consistency. CAPILENE ® T 12 EV is suitable for: spunbonded nonwoven fabric. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 26 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 32.0 | MPa | ASTM D638 |
| Yield | 30.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 2 | 12 | % | ASTM D638 |
| Yield | 12 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 1350 | MPa | ASTM D790 |
| -- 3 | 1250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 25 | J/m | ASTM D256 |
| 23°C | 3.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 109 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 80.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 155 | °C | ISO 306/A, ASTM D1525 4 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Veroplas SER20E | PlastxWorld Inc. | ABS | Veroplas |
| BMC 1902 | Bulk Molding Compounds, Inc. | Alkyd | BMC |
| ASI POLYPROPYLENE 829-01 | A. Schulman Inc. | PP Homopolymer | ASI POLYPROPYLENE |
| Karina RED COLOR CONCENTRATE 42/183-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hifax TYC 900X BLACK | LyondellBasell Industries | PP Copolymer | Hifax |