| RX® 790 is a fiberglass reinforced phenolic novolac compound, featuring a good balance of strength and toughness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.73 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.050 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 95 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, Compression Molded) | 105 | MPa | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 16000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 215 | MPa | ISO 178 |
| Compressive Stress | 380 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (Compression Molded) | 3.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/A | ||
| 1.8 MPa, Unannealed | 215 | °C | |
| 1.8 MPa, Annealed | > 282 | °C | |
| CLTE - Flow | 1.6E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.58 | W/m/K | ASTM C518 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 14 | kV/mm | ASTM D149 |
| Arc Resistance | 145 | sec | ASTM D495 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 282 | RTP Company | Nylon 66 | RTP |
| CompaMid® PA 6.6 GK 30 | DimeLika Plast GmbH | Nylon 66 | CompaMid® |
| KUBE PIR 22310 | KUBE Electronics AG | HDPE | KUBE PIR |
| Paxon™ EA55-003 | ExxonMobil Chemical | HDPE, UHMW | Paxon™ |
| 3M™ Dyneon™ Fluoroelastomer FE 5625N | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |