MAJORIS AT200
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Hcye7A_MAJORIS-AT200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AT200 is a natural, 20% mineral filled polypropylene compound intended for extrusion profile and blow moulding. AT200 has a rather low flow rate and outstanding process ability. The product is available in natural and black (AT200 - 8229) but other colours can be provided on request. APPLICATIONS
Products requiring excellent rigidity, low shrinkage and high dimensional stability can suitably be made from AT200. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.45 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.1 to 1.6 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 32.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1800 | MPa | ISO 178 |
| Flexural Stress | 45.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 73 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 120 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 69.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/A |
| Ball Pressure Test (125°C) | Pass | NF C 61-303 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 220 | °C | |
| Cylinder Zone 2 Temp. | 220 | °C | |
| Cylinder Zone 3 Temp. | 230 | °C | |
| Cylinder Zone 4 Temp. | 240 | °C | |
| Melt Temperature | 210 to 240 | °C | |
| Head Temperature | 240 | °C | |
| Die Temperature | 230 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ LC-20NCF/000 V3 Natural | PolyOne Corporation | LCP | Stat-Tech™ |
| Vydyne® R525H BK02 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Yanshan PE LD100 | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| Borlink™ LE0595-07 | Borealis AG | PE, Unspecified | Borlink™ |
| Cardia Biohybrid™ H-FM | Cardia Bioplastics™ | TPS+PP | Cardia Biohybrid™ |