Bergamid™ A700 G25 U-SO
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergamid™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HchKIU_Bergamid-A700-G25-U-SO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bergamid™ A700 G25 U-SO is a Polyamide 66 (Nylon 66) product filled with 25% glass fiber. It is available in Africa & Middle East, Asia Pacific, or Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.38 | g/cm³ | DIN 53479 |
| Ash Content | 25 | % | ISO 3451 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Use Temperature | IEC 60216 | ||
| -- 2 | 120 | °C | |
| Short Time | 220 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 8500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 160 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eA | ||
| -30°C | 60 | kJ/m² | |
| 23°C 3 | 65 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 250 | °C | ISO 75-2/B |
| Melting Temperature (DSC) | 261 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 80 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.50 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.015 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 400 to 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 to 3.00 mm, ALL) | V-0 | Internal Method | |
| Glow Wire Ignition Temperature 4(3.00 mm) | 960 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | ±0.02 g/cm³ |
| 2 . | Continuous (GTP 50% Tensile) |
| 3 . | Type 1 |
| 4 . | 0.8 mm wire |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NANCAR® 1051M50 | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| Hostalen PP H2250 36 | LyondellBasell Industries | PP Homopolymer | Hostalen PP |
| Karina BLACK PVC COMPOUND 70900-48/1-H-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Luran® 338L | Styrolution | SAN | Luran® |
| neogol® 70 P UG | API SpA | TPO (POE) | neogol® |