TOPAS® 8007S-04

Category:	COC , Cyclic Olefin Copolymer
Manufacturer:	Topas Advanced Polymers, Inc.
Trademark:	TOPAS®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Hatge8_TOPAS-8007S-04.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Product Description
TOPAS 8007S-04 is a general purpose injection molding grade. It is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for healthcare and other high-tech products. Lower leachables and extractables of TOPAS COC preserve content stability and quality. It is a non-polar substrate that does not promote adsorption, denaturation, aggregation, or precipitation like glass can. Analytical results are more accurate with TOPAS COC in contact with sensitive chemistries.

Selected Applications

Drug delivery

Prefilled syringes, vials, cartridges

Bottles and tubes

Surgical instruments

IV containers and components

Labware

Optics

Electronics

Food packaging

Healthcare and food contact

Leading Attributes

Low leachables & extractables, low water transmission

Non-ionic, does not promote adsorption like glass

Minimally reactive

Chemically resistant to alcohol, acetone, and acrylates

Transparent, withstands EtO and gamma sterilization

Temperature resistance, clarity and purity

Clarity, low birefringence, low moisture sensitivity

Low dielectric constant, thermoplastic

Not manufactured with BPA, phthalates, or halogens

Broad regulatory compliance

Related Grades for Injection Molding, Healthcare, Optics and Diagnostics

TOPAS 8007D-61 - externally lubricated 8007S-04 for blow molding of bottles, vials, etc.

TOPAS 8007X10 - our highest ultraviolet (UV) transmission grade

General Information
Features	High purity Low extract Moisture proof Radiation disinfection Copolymer Ethylene oxide disinfection Good chemical resistance Alcohol resistance Heat resistance, high Definition, high Compliance of Food Exposure General BPA-free amorphous Halogen-free
Uses	Electrical/Electronic Applications Pipe fittings Optical applications Bottle Laboratory apparatus Food packaging General Surgical instruments Drug packaging Medical/nursing supplies
Agency Ratings	DMF 12132 FDA FCN 405 ISO 10993 USP Class VI Europe 10/1/2011 12:00:00 AM
Appearance	Clear/transparent
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.02	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (260°C/2.16 kg)	29	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (260°C/2.16 kg)	32.0	cm³/10min	ISO 1133
Molding Shrinkage ¹	0.10 - 0.30	%	Internal method
Water Absorption (Saturation, 23°C)	0.010	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2600	MPa	ISO 527-2/1A/1
Tensile Stress (Yield)	63.0	MPa	ISO 527-2/1A/50
Tensile Strain (Yield)	4.5	%	ISO 527-2/1A/50

Films	Nominal Value	Unit	Test Method
Water Vapor Transmission Rate (23°C, 85% RH)	0.025	g·mm/m²/atm/24 hr	DIN 53122

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	3.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	20	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	75.0	°C	ISO 75-2/B
Glass Transition Temperature	78.0	°C	ISO 11357-2
Vicat Softening Temperature	80.0	°C	ISO 306/B50

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	> 1.0E+16	ohms·cm	IEC 60093
Relative Permittivity			IEC 60250
1 kHz	2.35		IEC 60250
10 kHz	2.35		IEC 60250
Comparative Tracking Index	> 600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	HB		UL 94

Optical	Nominal Value	Unit	Test Method
Refractive Index	1.530		ISO 489
Transmittance	91.0	%	ISO 13468-2

Injection	Nominal Value	Unit
Drying Temperature	50.0	°C
Drying Time	4.0 - 6.0	hr
Rear Temperature	190 - 220	°C
Middle Temperature	200 - 240	°C
Front Temperature	220 - 250	°C
Nozzle Temperature	220 - 250	°C
Processing (Melt) Temp	190 - 250	°C
Mold Temperature	40.0 - 70.0	°C
Injection Pressure	50.0 - 110	MPa
Injection Rate	Moderate-Fast
Holding Pressure	30.0 - 60.0	MPa
Back Pressure	< 15.2	MPa
Screw Speed	50 - 200	rpm

Injection instructions
Feed temperature: <60°C (<140°F)Max. residence time: <15 minutes; short interruptions to cycle reduce Tx = 170°C (338°F)Injection speed: 50 - 150 mm/sec (2.0 - 6.0 in/sec)Nozzle type: Free flow

Note Message
1 .	Dependent on processing conditions and part design.

Resin Grade	Manufacturer	Category	Trademark
RTP 385 TFE 15 FR	RTP Company	PC	RTP
TYRIN™ 6000	The Dow Chemical Company	CPE	TYRIN™
Dynaprene® VE2173A	Nantex Industry Co., Ltd.	TPE	Dynaprene®
HiFill® PC GF30 X	Techmer Engineered Solutions	PC	HiFill®
Novalloy-S S1210	PlastxWorld Inc.	PC+ABS	Novalloy-S