Lotryl® BESTPEEL 2407
| Category: | EMA , Ethylene Methyl Acrylate Copolymer |
| Manufacturer: | Arkema |
| Trademark: | Lotryl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Habi5O_Lotryl-BESTPEEL-2407.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LOTRYL® BESTPEEL 2407 is a ready-to-use thermoplastic composition designed to make peelable heat seal layers onto various substrates. The base resin is a random copolymer of ethylene and methyl acrylate, polymerized by high-pressure process in autoclave reactor. Modification is introduced to ensure the best processability in the different film technologies, and the suitable properties in heat sealing and peeling. Applications LOTRYL® BESTPEEL 2407 is used as top layer of laminates in order to provide the functions of heat sealability onto various substrates like PP, PS, PET and PVC, and easy opening by interfacial peeling. LOTRYL® BESTPEEL 2407 is easily processed using the technologies of coextrusion coating, cast film coextrusion, blown film coextrusion or sheet coextrusion, to produce multilayers that can be used as lids, either directly or after lamination with other films. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 to 8.0 | g/10 min | ASTM D1238, ISO 1133 |
| Methyl Acrylate Content | 23.0 to 25.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, Compression Molded) | 79 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Break | 6.00 | MPa | ASTM D638 |
| Break, Compression Molded | 6.00 | MPa | ISO 527-2 |
| Tensile Elongation (Break, Compression Molded) | 750 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (Compression Molded) | 10.0 | MPa | ASTM D790, ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | < 40.0 | °C | ISO 306/A, ASTM D1525 1 |
| Melting Temperature | 69.0 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 117 V33 BLACK 61 LP | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| NILAMID® A3 GB30 TF20 | Nilit Plastics | Nylon 66 | NILAMID® |
| Catalyst CT/5 UV | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| Generic PUR-Est/eth,TDI | Generic | PUR-Est/eth,TDI | Generic |
| Vyncolit® X7530 | SBHPP | Phenolic | Vyncolit® |