LNP™ LUBRICOMP™ 9X06483 compound
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HYMYoF_LNP-LUBRICOMP-9X06483-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* 9X06483 is a compound based on a Nylon 4/6 containing PTFE. Added features of this grade are: Heat Stabilized, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound STN-L-4030 HS Product reorder name: 9X06483 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.29 | g/cm³ | ASTM D792 |
| -- | 1.28 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 2.0 to 4.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 1.8 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.7 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3130 | MPa | ASTM D638 |
| -- | 3010 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 80.0 | MPa | ASTM D638 |
| Yield | 78.0 | MPa | ISO 527-2/5 |
| Break 3 | 74.0 | MPa | ASTM D638 |
| Break | 76.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 5.8 | % | ASTM D638 |
| Yield | 6.5 | % | ISO 527-2/5 |
| Break 5 | 5.9 | % | ASTM D638 |
| Break | 6.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2960 | MPa | ASTM D790 |
| -- 7 | 2800 | MPa | ISO 178 |
| Flexural Stress | 101 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.32 | ||
| vs. Itself - Static | 0.32 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | -0.0500 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 11.5 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 52 | J/m | ASTM D256 |
| 23°C 8 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 920 | J/m | ASTM D4812 |
| 23°C 9 | 56 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 3.60 | J | ASTM D3763 |
| -- | 0.800 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 283 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 276 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 151 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 92.0 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT4802-01 | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| STERLENE™ BMU130D | R&P (Pte.) Ltd. | TPO (POE) | STERLENE™ |
| Wah Hong UP WH-8100-BLK D | Wah Hong Industrial Corp. | Polyester Alloy | Wah Hong UP |
| Infino XP-2140C | SAMSUNG SDI CO., LTD. | PPS | Infino |
| SABIC® PPcompound G3240A | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |