UBE Nylon 1018I
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | UBE Industries, Ltd. |
| Trademark: | UBE Nylon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HY1KUG_UBE-Nylon-1018I.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High impact resistant |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 1.5 | % | |
| Flow | 1.1 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.6 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1400 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 50 | % | ISO 527-2 |
| Flexural Modulus | 1400 | MPa | ISO 178 |
| Flexural Stress | 55.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 150 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 75.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™ LA543 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| Ultradur® S 4090 G2 | BASF Corporation | PBT+ASA | Ultradur® |
| Karina WHITE PVC COMPOUND 900-10/ 1-P-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LONGLITE® PBT 7020-104X | CCP Group | PBT+ASA | LONGLITE® PBT |
| Dow Corning® C6-540 | Dow Corning Corporation | Silicone | Dow Corning® |