LNP™ THERMOCOMP™ LC006 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HWfuCH_LNPTHERMOCOMPLC006compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOCOMP LC006 is a compound based on Polyetheretherketone containing Carbon Fiber. Added features include: Electrically Conductive. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 23400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 219 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.7 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 17000 | MPa | ISO 178 |
| Flexural Stress | 301 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | > 300 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 6.9E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 4.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 - 1.0E+6 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 349 - 360 | °C | |
| Middle Temperature | 366 - 377 | °C | |
| Front Temperature | 382 - 393 | °C | |
| Processing (Melt) Temp | 382 - 388 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu RTV KE-1833 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| D-MEC SCR9120 | D-MEC Ltd. | Epoxy | D-MEC |
| IROGRAN® A 78 P 4766 | Huntsman Corporation | TPU-Polyether | IROGRAN® |
| LNP鈩?THERMOCOMP鈩?OF008G compound | SABIC Innovative Plastics | PPS, Linear | LNP™ THERMOCOMP™ |
| Hifax TYC 2052P | LyondellBasell Industries | PP Copolymer | Hifax |