GLAMIDE® T-422VOR
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HWQtKf_GLAMIDE-T-422VOR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GLAMIDE®T-422VOR is a polyamide 6 (nylon 6) product, which contains a 23% mineral filler. It is available in North America. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.56 | -- | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 20 | -- | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.10 - 0.20 | -- | % | ASTM D955 |
| 3.00 mm | 0.30 - 0.60 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 24 hr | 0.50 | -- | % | ASTM D570 |
| Equilibrium, 65% RH | 1.8 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 65.0 | 61.0 | MPa | ASTM D638 |
| Yield, 23°C | 51.0 | 38.0 | MPa | ASTM D638 |
| Yield, 80°C | 28.0 | 24.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 1.5 | 4.5 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 7200 | 6400 | MPa | ASTM D790 |
| 23°C | 6100 | 4400 | MPa | ASTM D790 |
| 80°C | 3400 | 1200 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 110 | 104 | MPa | ASTM D790 |
| Yield, 23°C | 90.0 | 63.0 | MPa | ASTM D790 |
| Yield, 80°C | 50.0 | 38.0 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 62.0 | 45.0 | MPa | ASTM D695 |
| Taber Abrasion Resistance (1000 Cycles, CS-17 Wheel) | 32.0 | -- | mg | ASTM D1044 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 30 | 45 | J/m | ASTM D256 |
| 23°C | 40 | 70 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 205 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 160 | -- | °C | ASTM D648 |
| CLTE - Flow | 4.2E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 29 | 20 | kV/mm | ASTM D149 |
| Arc Resistance | 25.0 | 15.0 | sec | ASTM D495 |
| Comparative Tracking Index | 350 | 350 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.730 mm) | V-0 | -- | UL 94 |
| Additional Information |
|---|
| 调节后的 Volume Resistivity, ASTM D257: 1e9 to 1e10 ohm-m |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 250 - 285 | °C | |
| Mold Temperature | 60.0 | °C | |
| Injection Pressure | 40.0 - 60.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Borcoat™ HE7405 | Borealis AG | HDPE | Borcoat™ |
| HiFill® TPU 1000 | Techmer Engineered Solutions | TPU, Unspecified | HiFill® |
| Huafon JF-W-BK3045 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Jiangsu Sinarise EI9000X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| Lupol® GP2300 | LG Chem Ltd. | PP, Unspecified | Lupol® |