LEXAN™ LUX1169 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HWNDu3_LEXAN-LUX1169-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN LUX1169 |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 21.0 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.35 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 60.0 | MPa | |
| Break | 50.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 6.0 | % | |
| Break | 60 | % | |
| Flexural Modulus 1 | 2400 | MPa | ISO 178 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2 | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 60 | kJ/m² | |
| Charpy Unnotched Impact Strength 3 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength 4 | ISO 180/1A | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 60 | kJ/m² | |
| Unnotched Izod Impact Strength 5 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 140 | °C | ISO 306/B50 |
| -- | 141 | °C | ISO 306/B120 |
| CLTE - Transverse (-40 to 40°C) | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*3 sp=62mm |
| 3 . | 80*10*3 sp=62mm |
| 4 . | 80*10*3 |
| 5 . | 80*10*3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Preformance™ PET 1708 | StarPet Inc. | PET | Preformance™ PET |
| Ad-Tech Epoxy EL-324-1 | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| Kumho SBR 1712P | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |
| Lucent PP CPP-0307 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |
| PLEXIGLAS® Sheet Optical CLear 0Z003 | Evonik Industries AG | Acrylic (PMMA) | PLEXIGLAS® Sheet |