Lupol® HF3308C
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HUdzxK_Lupol-HF3308C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lupol® HF3308C is a Polypropylene material filled with 30% mineral. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Lupol® HF3308C are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.70 to 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 24.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 50 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 2840 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 40.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 5(23°C) | 52 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 135 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Minimum Moisture Content | 0.010 | % | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 200 to 230 | °C | |
| Front Temperature | 200 to 230 | °C | |
| Nozzle Temperature | 210 to 230 | °C | |
| Processing (Melt) Temp | 200 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 30 mm/min |
| 4 . | 30 mm/min |
| 5 . | 6.4 mm Notch Depth |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 7109M | Chevron Phillips Chemical Company LLC | LLDPE | MarFlex® |
| RTP 4085 TFE 5 | RTP Company | PPA | RTP |
| ACRYLITE® Heatresist hw55 | Evonik Cyro LLC | Acrylic (PMMA) | ACRYLITE® |
| FLEXITEQ™ F60A111UV | Marplex Australia Pty. Ltd. | TPV | FLEXITEQ™ |
| Lucent PP PPC-310 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |