Andur 2-95 AP/Curene® 442
| Category: | PUR-Ether/TDI , Polyurethane (Polyether, TDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HTMgZg_Andur-2-95-AP-Curene-442.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Andur 2-95AP is a polyether (PTMG) based liquid, toluene diisocyanate terminated prepolymer. An elastomer with a hardness of 95 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by curing Andur 2-95AP with polyols and their combination with Curene 442 and other diamines, or through the use of plasticizers. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ASTM D1505 |
| Molding Shrinkage - Flow | 1.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 95 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 5% strain | 1.16 | MPa | ASTM D695 |
| 10% strain | 4.12 | MPa | ASTM D695 |
| 15% strain | 6.92 | MPa | ASTM D695 |
| 25% strain | 10.7 | MPa | ASTM D695 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 13.9 | MPa | ASTM D412 |
| 300% strain | 28.3 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 50.6 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 420 | % | ASTM D412 |
| Compression Set | 30 | % | ASTM D395B |
| Bayshore Resilience | 42 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 4.0 - 6.0 | min | |
| Demold Time | 30 | min | |
| Post Cure Time (96°C) | 16 | hr |
| Additional Information |
|---|
| Durometer Hardness, ASTM D2240, Shore A: 93 to 97Die C Tear, ASTM D1004: 575 pliAverage Split Tear, ASTM D1938: 205 pliStoichiometry Curative Level: 95%Mix Temperature: Andur 2-95 AP: 180-212°F Curene 442: 235-250°F |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 104 - 113 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® D6770 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RTP PA66 33 GF BLK/BLK | RTP Company | Nylon 66 | RTP |
| Small Boss RPVC01 | Tongxiang Small Boss Special Plastic Products Co., Ltd. | PVC, Rigid | Small Boss |
| Hostacom ERC 161N C21451 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sylvin 7011EE-60 WHITE 1161 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |