Fortron® 1131L4 ITT
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Fortron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HS9uIh_Fortron-1131L4-ITT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fortron®1131L4 ITT is a polyphenylene sulfide (PPS) product, which contains a 30% glass fiber reinforced material. It is available in North America, Africa and the Middle East, Latin America or Europe. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.40 | g/cm³ | ASTM D792 |
| -- | 1.56 | g/cm³ | ISO 1183 |
| Specific Volume | 0.715 | cm³/g | ASTM D792 |
| Molding Shrinkage | |||
| Flow | 1.0 | % | ASTM D955 |
| Transverse flow | 0.80 | % | ASTM D955 |
| Vertical flow direction | 0.50 - 0.80 | % | ISO 294-4 |
| Flow direction | 0.30 - 0.70 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class m | 93 | ASTM D785 | |
| M scale | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12200 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, 23°C | 86.2 | MPa | ASTM D638 |
| Fracture | 165 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.9 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 12000 | MPa | ISO 178 |
| Flexural Stress 1 | 255 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 42 | kJ/m² | ISO 179/1eU |
| 23°C | 42 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 8.0 | kJ/m² | ISO 180/1A |
| 23°C | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, annealed | 200 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 105 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 265 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 205 | °C | ISO 75-2/C |
| Glass Transition Temperature 2 | 90.0 | °C | ISO 11357-2 |
| Melting Temperature 3 | 280 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 2.9E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 6.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| -- | 1.0E+16 | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 3.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 9.0E-3 | ASTM D150 | |
| Arc Resistance | 124 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.380 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 140 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 290 - 300 | °C | |
| Middle Temperature | 310 - 320 | °C | |
| Front Temperature | 330 - 340 | °C | |
| Nozzle Temperature | 310 - 330 | °C | |
| Processing (Melt) Temp | 330 - 340 | °C | |
| Mold Temperature | 140 - 160 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 330 to 340°CZone 4 Temperature: 330 to 340°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | Break |
| 2 . | 10°C/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4099 X 128641 B | RTP Company | PPA | RTP |
| RAMOFIN PPC301G2 | Polyram Ram-On Industries | PP Copolymer | RAMOFIN |
| Braskem PP RP 250 | Braskem America Inc. | PP Random Copolymer | Braskem PP |
| Hanwha Total PP RF401 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Plastiglas Chemcast® HI | Plastiglas de Mexico S.A de C.V. | Acrylic, Unspecified | Plastiglas |