S-RIM™ 6260 Black
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Hapco Inc. |
| Trademark: | S-RIM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HRD67q_S-RIM-6260-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
S-RIM™ 6260 Black is a Thermoplastic product. It can be processed by structural react. inject. molding (srim) and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D4669 |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D2566 |
| Weight - per cubic inch | 18 | g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 1(25°C) | 1.0 | min | ASTM D2971 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 655 | MPa | ASTM D638 |
| Tensile Strength | 53.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 15 | % | ASTM D638 |
| Flexural Modulus | 1820 | MPa | ASTM D790 |
| Flexural Strength | 73.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 9.6 | J/m | ASTM D256 |
| Unnotched Izod Impact | 56 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed 2 | 189 | °C | |
| 0.45 MPa, Unannealed 3 | 108 | °C | |
| 1.8 MPa, Unannealed 4 | 117 | °C | |
| 1.8 MPa, Unannealed 5 | 157 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 86, Mix Ratio by Volume: 100 | ||
| Thermoset Mix Viscosity (25°C) | 600 | cP | ASTM D4878 |
| Demold Time (21°C) | 5.0 to 12 | min | Internal Method |
| Note Message | |
|---|---|
| 1 . | 100 g |
| 2 . | post cured at 140°C |
| 3 . | post cured at 80°C |
| 4 . | post cured at 80°C |
| 5 . | post cured at 140°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TES J-1200/20/VO/Natl | Techmer Engineered Solutions | ABS | TES |
| WELLAMID Nylon 6000 GS 40 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Next Nylon 66 Prime Series PX-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| KumhoSunny ABS 744 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| Hostacom EKC 133N G71526 | LyondellBasell Industries | PP Copolymer | Hostacom |