EL-Lene™ H6670B
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Lene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HQ1XNK_EL-Lene-H6670B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-Lene H6670B is a high density polyethylene resin suitable for producing milk bottles by using Extrusion blow molding machine. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.966 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 25% Igepal, Compression Molded, F50) | 24.0 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 68 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 31.4 | MPa | |
| Break | 32.4 | MPa | |
| Tensile Elongation 2(Break) | 1200 | % | ASTM D638 |
| Flexural Modulus | 1470 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 128 | °C | ASTM D1525 |
| Melting Temperature | 132 | °C | ASTM D2117 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 180 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VICTREX® PEEK 450FE20 | Victrex plc | PEEK | VICTREX® PEEK |
| 4LEX® 25F10000 | 4Plas | PC | 4LEX® |
| Geon™ Vinyl Flexible R7426A | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Osterlene® PPR02CLNX | Osterman & Company | PP Random Copolymer | Osterlene® |
| Styroflex® 2G66 | INEOS Styrolution Group GmbH | SBC | Styroflex® |