Silastic® Q7-4565

Category:	Silicone , Silicone
Manufacturer:	Dow Corning Corporation
Trademark:	Silastic®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	HNecga_SilasticQ74565.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Enhanced Tear Resistant (ETR) High Consistency Rubber silicone elastomers for peroxide cure APPLICATIONS SILASTIC BioMedical Grade ETR Elastomers (Q7-4535, Q7-4550, Q7-4565) are uncatalyzed elastomer materials designed for compounding into elastomer for part fabrication and medical devices. DESCRIPTION SILASTIC BioMedical Grade ETR Elastomers (Q7-4535, Q7-4550, Q7-4565) are a series of one-part uncatalyzed silicone elastomer raw materials. The addition of a peroxide catalyst is necessary to accomplish vulcanization. The resulting elastomers range in hardness from soft to firm (nominally 35 to 65, Shore A Durometer). These materials may be blended if desired to achieve intermediate hardnesses. After appropriate compounding with a peroxide catalyst, cure and post-cure, the elastomers are heat stable up to 204°C (400°F), can be autoclaved, and exhibit high gas permeability compared with most thermoset elastomers and thermoplastics.

Message

Enhanced Tear Resistant (ETR) High Consistency Rubber silicone elastomers for peroxide cure

APPLICATIONS
SILASTIC BioMedical Grade ETR Elastomers (Q7-4535, Q7-4550, Q7-4565) are uncatalyzed elastomer materials designed for compounding into elastomer for part fabrication and medical devices.

DESCRIPTION
SILASTIC BioMedical Grade ETR Elastomers (Q7-4535, Q7-4550, Q7-4565) are a series of one-part uncatalyzed silicone elastomer raw materials. The addition of a peroxide catalyst is necessary to accomplish vulcanization.

The resulting elastomers range in hardness from soft to firm (nominally 35 to 65, Shore A Durometer). These materials may be blended if desired to achieve intermediate hardnesses.

After appropriate compounding with a peroxide catalyst, cure and post-cure, the elastomers are heat stable up to 204°C (400°F), can be autoclaved, and exhibit high gas permeability compared with most thermoset elastomers and thermoplastics.

General Information
Features	High Gas Permeability High pressure heating resistance
Uses	Composite Medical/nursing supplies
Agency Ratings	EP Unspecified Rating ISO 10993-Part I USP Class VI
Processing Method	Composite

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.20	g/cm³	ASTM D792

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	63		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress (200% Strain)	2.80	MPa	ASTM D412
Tensile Strength	7.90	MPa	ASTM D412
Tensile Elongation (Break)	660	%	ASTM D412
Tear Strength ¹	47.0	kN/m	ASTM D624

Additional Information
Values are for samples crosslinked with Perkadox PD-505.

Note Message
1 .	B mould

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC P8190	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
SUMILITE® PVC VSS-1104	Sumitomo Bakelite Co., Ltd.	PVC, Unspecified	SUMILITE® PVC
EPIMIX PBT GFR 30 NC	EPSAN Plastik SAN. ve TiC. A.S.	PBT	EPIMIX
Lucky Enpla LHLD1007	Lucky Enpla Co LTD	PC	Lucky Enpla
ESTOPLAST ZK 6415BB01	Ester Industries Ltd.	PC	ESTOPLAST ZK