N66AN is a fast cycling, general purpose unfilled injection moulding grade of nylon 66.
General Information
Features
  • Fast molding cycle
  • General
Uses
  • General
Processing Method
  • Injection molding
PhysicalDryConditionedUnitTest Method
Density 1.14--g/cm³ISO 1183
Molding Shrinkage 11.5 - 2.0--%Internal method
MechanicalDryConditionedUnitTest Method
Tensile Modulus 28001500MPaISO 527-2
Tensile Stress (Yield)80.060.0MPaISO 527-2
Flexural Modulus 30001000MPaISO 178
Flexural Stress 295.035.0MPaISO 178
ImpactDryConditionedUnitTest Method
Notched Izod Impact 7.0 kJ/m²No BreakISO 180
ThermalDryConditionedUnitTest Method
Heat Deflection Temperature
     0.45 MPa, not annealed 220200°CISO 75-2/B
     1.8 MPa, not annealed 90.075.0°CISO 75-2/A
ElectricalDryConditionedUnitTest Method
Surface Resistivity 1.0E+151.0E+10ohmsIEC 60093
Volume Resistivity 1.0E+151.0E+12ohms·cmIEC 60093
Dielectric Strength (3.00 mm)1812kV/mmIEC 60243-1
Relative Permittivity (1 MHz)3.804.30IEC 60250
Dissipation Factor (1 MHz)0.0200.080IEC 60250
Comparative Tracking Index > 600> 600VIEC 60112
InjectionDryUnit
Drying Temperature 80.0 - 100°C
Drying Time 2.0hr
Rear Temperature 270 - 290°C
Middle Temperature 270 - 290°C
Front Temperature 270 - 290°C
Processing (Melt) Temp < 300°C
Mold Temperature 60.0 - 80.0°C
Injection Rate Moderate
Screw Speed 50 - 200rpm
Injection instructions
Back Pressure: Low to mediumInjection Pressure: MediumNo drying is necessary unless the material has been exposed to air for longer than 3 hours.
Note Message
1 .Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions.The range values stated were determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).
2 .At conventional deflection
Resin Grade Manufacturer Category Trademark
RTP 1201-80D RTP Company TPU-Polyester RTP
DIOSHY® AB-820EM DIOSHY Co.,Ltd. SEBS DIOSHY®
FHR EPS 40-3640 Flint Hills Resources, LP PS (EPS) FHR EPS
HFFR 2004 Teknor Apex Company Polyolefin, Unspecified HFFR
Petrothene® XL07417 LyondellBasell Industries Polyolefin, Unspecified Petrothene®