LG ABS BM662B
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HLtaB8_LG-ABS-BM662B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LG ABS BM662B is an acrylonitrile butadiene styrene (ABS) material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is blow molding. The main characteristics of LG ABS BM662B are: heat resistance. Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 46.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 15 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2060 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 69.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 69 | J/m | ASTM D256 |
| -30°C, 6.40 mm | 59 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 160 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 110 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 103 | °C | ASTM D648 |
| Vicat Softening Temperature | 110 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 180 - 200 | °C | |
| Cylinder Zone 2 Temp. | 190 - 210 | °C | |
| Cylinder Zone 3 Temp. | 190 - 210 | °C | |
| Cylinder Zone 4 Temp. | 200 - 220 | °C | |
| Adapter Temperature | 220 | °C | |
| Melt Temperature | 200 - 210 | °C | |
| Die Temperature | 220 | °C |
| Extrusion instructions |
|---|
| Processing information given is for Blow Molding.Minimum Moisture Content: <0.07% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadraflex™ ARE-85A-B20 | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| TPC PVC SG760 | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| AIE ABS S20G2 | Asia International Enterprise (Hong Kong) Limited | ABS | AIE ABS |
| Braskem PE STN7006 | Braskem America Inc. | LDPE | Braskem PE |
| KEBAFORM® C 902 FA | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |