EEC MD 3804 U
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | Egyptian European Company |
| Trademark: | EEC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HLYGfA_EEC-MD-3804-U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PCC MD 3804 U is a Polyethylene product. It can be processed by rotational molding and is available in Africa & Middle East or Europe. Applications of PCC MD 3804 U include consumer goods, containers, household applications and tanks. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ISO 1872-1 |
| Apparent Density | 0.37 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (23°C, F50) | 200 | hr | ASTM D1693 |
| Particle Size - Medium | < 500 | µm | ASTM D1921 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fluidity 1 | 31.0 | sec | ASTM D1895 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 18.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1400 | % | ISO 527-2 |
| Flexural Modulus | 750 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 20 | kJ/m² | ISO 179 |
| Note Message | |
|---|---|
| 1 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 GB 10 FR | RTP Company | PC | RTP |
| Toyolac® 450Y MH5 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| Ultramid® B24 NSD 05 | BASF Corporation | Nylon 6 | Ultramid® |
| HI-ZEX™ 1700J | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |
| Karina PINK COLOR CONCENTRATE 39/32-GI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |