Pearlthane® 11T85UV
| Category: | TPU-Capro , Thermoplastic Polyurethane Elastomer (Polycaprolactone) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HKGP4S_Pearlthane-11T85UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PEARLTHANE® 11T85UV is a UV resistant polycaprolactone copolyester based TPU, supplied in form of translucent, colourless pellets, featuring adequate hardness with excellent flow and mechanical properties. It can be injection-molded and coextruded. PEARLTHANE® 11T85UV when processed by injection moulding, can be used for making automotive parts and a variety of technical components. PEARLTHANE® 11T85UV when processed by coextrusion, can be used for making technical sheets thanks to its excellent adhesion into polar substrates such as ABS, PC and PVC. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.16 | g/cm³ | ASTM D792 |
| 20°C | 1.16 | g/cm³ | ISO 2781 |
| Moisture Content | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 25.0 | mm³ | ISO 4649 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 86 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 527 | ||
| 100% strain | 6.00 | MPa | ASTM D412, ISO 527 |
| 300% strain | 10.0 | MPa | ASTM D412, ISO 527 |
| Tensile Strength (Yield) | 40.0 | MPa | ASTM D412, ISO 527 |
| Tensile Elongation (Break) | 630 | % | ASTM D412, ISO 527 |
| Tear Strength | |||
| -- 1 | 90.0 | kN/m | ASTM D624 |
| -- | 90 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395B | ||
| 23°C, 70 hr | 20 | % | ASTM D395B |
| 70°C, 22 hr | 35 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 2 | -40.0 | °C | ISO 11357-2 |
| Melting Temperature 3 | 178 - 188 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Rear Temperature | 195 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 210 | °C | |
| Mold Temperature | 35.0 | °C |
| Injection instructions |
|---|
| Closing force: : 30 tonsScrew diameter: : 30 mmMaximum hydraulic pressure: : 210 barMould: : Plaque 120x120x2 mmL/D ratio: : 23 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Cylinder Zone 1 Temp. | 175 - 195 | °C | |
| Cylinder Zone 2 Temp. | 185 - 205 | °C | |
| Cylinder Zone 3 Temp. | 195 - 215 | °C | |
| Cylinder Zone 4 Temp. | 200 - 220 | °C | |
| Die Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| Extruder Speed: 20 to 50rpmExtrusion Compression Ratio: 2:1 to 3:1Extrusion L/D Ratio: 25:1 to 30:1 |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | 10°C /min |
| 3 . | Temperature at which MFI = 10 g/10 min @ 21.6 kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1499 X 92453 | RTP Company | PESU | RTP |
| Generic Nylon 6 Elast | Generic | Nylon 6 Elast | Generic |
| Karina GRAY COLOR CONCENTRATE 18/ 90-RG-GE (CS) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LubriOne™ LubriOne™ AT-10AF/15T Natural | PolyOne Corporation | Acetal (POM) Copolymer | LubriOne™ |
| MAGNUM™ 1250 BG | Trinseo | ABS | MAGNUM™ |