Nucrel® 31001
| Category: | EAA , Ethylene Acrylic Acid Copolymer |
| Manufacturer: | DuPont Packaging & Industrial Polymers |
| Trademark: | Nucrel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HHlt4o_Nucrel-31001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nucrel® 31001 is a copolymer of ethylene and acrylic acid, made with nominally 9.5 wt% acrylic acid. It is available for use in blown and cast film extrusion and coextrusion equipment. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.940 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.3 | g/10 min | ASTM D1238, ISO 1133 |
| Acrylic Acid Content | 9.5 | wt% |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 79.0 | °C | ASTM D1525, ISO 306 |
| Melting Temperature | 99.0 | °C | DSC, ISO 3146 |
| Freezing Point | |||
| -- | 80 | °C | ISO 3146 |
| -- | 80 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 135 | °C | |
| Cylinder Zone 2 Temp. | 160 | °C | |
| Cylinder Zone 3 Temp. | 185 | °C | |
| Cylinder Zone 4 Temp. | 185 | °C | |
| Cylinder Zone 5 Temp. | 185 | °C | |
| Adapter Temperature | 185 | °C | |
| Melt Temperature | < 285 | °C | |
| Die Temperature | 185 | °C |
| Extrusion instructions |
|---|
| Processing conditions shown are for blown film. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Teslin® SP 1200 | PPG Industries, Inc. | PE, Unspecified | Teslin® |
| FLEXAREN® 14006 | Innospec Leuna GmbH | EVA | FLEXAREN® |
| Fluoroplex F 30 - GML | UNIFLON | PTFE | Fluoroplex |
| Elastron® V V100.A73.B | Elastron USA, Inc. | TPV | Elastron® V |
| Mitsui EPT™ 3092M | Mitsui Chemicals, Inc. | EPDM | Mitsui EPT™ |