| 6% multi-walled carbon nanotubes dispersed in a polypropylene matrix suitable injection molding applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.938 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ASTM D638 |
| Tensile Strength | 33.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.5 | % | ASTM D638 |
| Flexural Modulus | 1790 | MPa | ASTM D790 |
| Flexural Strength | 53.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 19 | J/m | ASTM D256 |
| Unnotched Izod Impact | 470 | J/m | ASTM D256 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.5E+3 | ohms | ASTM D257 |
| Volume Resistivity | 2.3E+6 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 149 - 232 | °C | |
| Middle Temperature | 149 - 232 | °C | |
| Front Temperature | 149 - 232 | °C | |
| Nozzle Temperature | 149 - 232 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michilex M5000 | API Polymers, Inc. | PC | Michilex |
| Monprene® RG-20160 X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |
| DOW™ HDPE TCP-2495 NT | The Dow Chemical Company | HDPE | DOW™ HDPE |
| COSMOPLENE® AR564 | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Copolymer | COSMOPLENE® |
| MBA PS 3124 | MBA Polymers Austria Kunststoffverarbeitung GmbH | PS (HIPS) | MBA PS |