Telcar® TL-88-N809C
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Telcar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HGp5Pw_Telcar-TL-88-N809C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Telcar TL-88-N809-C is a general purpose thermoplastic elastomer designed for the industrial market. Telcar TL-88-N809-C is suitable for injection molding and extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 4.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 1 second, injection molding | 53 | ASTM D2240 | |
| Shore D, 5 seconds, injection molding | 51 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Transverse flow : 100% strain 1 | 11.3 | MPa | ASTM D412 |
| Flow : 100% strain 2 | 16.8 | MPa | ASTM D412 |
| Transverse flow : 300% strain 3 | 11.6 | MPa | ASTM D412 |
| Tensile Strength 4 | ASTM D412 | ||
| Transverse flow : Fracture | 15.2 | MPa | ASTM D412 |
| Flow : Fracture | 17.8 | MPa | ASTM D412 |
| Tensile Elongation 5 | ASTM D412 | ||
| Transverse flow : Fracture | 790 | % | ASTM D412 |
| Flow : Fracture | 250 | % | ASTM D412 |
| Tear Strength 6 | ASTM D624 | ||
| Transverse flow | 86.9 | kN/m | ASTM D624 |
| Flow | 143 | kN/m | ASTM D624 |
| Compression Set 7 | ASTM D395B | ||
| 23°C, 22 hr | 61 | % | ASTM D395B |
| 70°C, 22 hr | 86 | % | ASTM D395B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 171 - 193 | °C | |
| Middle Temperature | 177 - 199 | °C | |
| Front Temperature | 182 - 204 | °C | |
| Nozzle Temperature | 188 - 210 | °C | |
| Processing (Melt) Temp | 188 - 210 | °C | |
| Mold Temperature | 25.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 166 - 188 | °C | |
| Cylinder Zone 2 Temp. | 171 - 193 | °C | |
| Cylinder Zone 3 Temp. | 177 - 199 | °C | |
| Cylinder Zone 5 Temp. | 182 - 204 | °C | |
| Die Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Note Message | |
|---|---|
| 1 . | Mouth die C, 510mm/min |
| 2 . | Mouth die C, 510mm/min |
| 3 . | C mold, 510mm/min |
| 4 . | C mold, 510mm/min |
| 5 . | Mouth die C, 510mm/min |
| 6 . | C mold, 510mm/min |
| 7 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201.3 SI 2 HS | RTP Company | Nylon 66 | RTP |
| Ranger PBT PBT-201-G30 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| VENELENE® 11Q4 | Poliolefinas Internacionales, C.A. (Polinter) | LLDPE | VENELENE® |
| HiFill FR® ABS FR AS | Techmer Engineered Solutions | ABS | HiFill FR® |
| Hipolyene 8021 HC | Zylog Plastalloys | TPO (POE) | Hipolyene |