HiFill® PA4/6 GF50 HS BK
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HEW6N4_HiFill-PA4-6-GF50-HS-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill® PA4/6 GF50 HS BK is a Polyamide 46 (Nylon 46) product filled with 50% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.62 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.2 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 165 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 9650 | MPa | ASTM D790 |
| Flexural Strength | 214 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 285 | °C | ASTM D648 |
| CLTE - Flow | 5.9E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 28 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 282 to 316 | °C | |
| Middle Temperature | 282 to 316 | °C | |
| Front Temperature | 282 to 316 | °C | |
| Processing (Melt) Temp | 246 to 316 | °C | |
| Mold Temperature | 87.8 to 127 | °C | |
| Back Pressure | 0.00 to 0.345 | MPa | |
| Screw Speed | 40 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 1060 | RTP Company | PBT | RTP |
| Monprene® CP-19041 | Teknor Apex Company | TPE | Monprene® |
| Fluoraz 890 | Greene, Tweed & Co. | PTFE | Fluoraz |
| Lupol® HI5204B | LG Chem Ltd. | TPO | Lupol® |
| LTP PA6125 | Chengdu Letian Plastics Co., Ltd | TP, Unspecified | LTP |