Monprene® RG-20160 X (PRELIMINARY DATA)
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Monprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HERHs6_Monprene-RG-20160-X-PRELIMINARY-DATA-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Monprene RG-20160 is specifically designed for regulated applications including food contact, toys, and children's products. This grade is suitable for extrusion. Monprene RG-20160 complies with various US FDA and European regulations and directives for food contact and toy safety. Please contact Teknor Apex for a regulatory compliance letter. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.886 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 1.5 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 5 sec) | 60 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 37 | ||
| Transverse flow : 100% strain | 1.80 | MPa | ISO 37 |
| Flow : 100% strain | 4.00 | MPa | ISO 37 |
| Tensile Stress 2 | ISO 37 | ||
| Transverse flow : Fracture | 9.00 | MPa | ISO 37 |
| Flow : Fracture | 4.00 | MPa | ISO 37 |
| Tensile Elongation 3 | ISO 37 | ||
| Transverse flow : Fracture | 800 | % | ISO 37 |
| Flow : Fracture | 150 | % | ISO 37 |
| Compression Set 4 | ISO 815 | ||
| 23°C, 22 hr | 16 | % | ISO 815 |
| 70°C, 22 hr | 28 | % | ISO 815 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 206 sec^-1) | 286 | Pa·s | ASTM D3835 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 149 - 160 | °C | |
| Cylinder Zone 2 Temp. | 160 - 204 | °C | |
| Cylinder Zone 3 Temp. | 171 - 216 | °C | |
| Cylinder Zone 4 Temp. | 182 - 227 | °C | |
| Die Temperature | 182 - 227 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 30 to 100 rpmDrying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150F (65C). |
| Note Message | |
|---|---|
| 1 . | Type 1, 510mm/min |
| 2 . | Type 1, 510mm/min |
| 3 . | Type 1, 510mm/min |
| 4 . | Type a |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Generic PP, Unspecified - Glass Fiber | Generic | PP, Unspecified | Generic |
| Hostacom PPR 4170L | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Karina BLACK PVC COMPOUND 750D48/ 1-DY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina WHITE PVC COMPOUND 800-10/61-Y-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupox® TE5011 | LG Chem Ltd. | PC+PBT | Lupox® |