Jamplast JPHDPEHMW
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | Jamplast, Inc. |
| Trademark: | Jamplast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HELprv_Jamplast-JPHDPEHMW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| JPHDPEHMW is a high molecular weight, high density polyethylene copolymer. This resin has superior stress crack resistance, high impact strength and good rigidity. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.949 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.10 | g/10 min | |
| 190°C/21.6 kg | 10 | g/10 min | |
| Environmental Stress-Cracking Resistance (100% Igepal, Compression Molded) | 800 | hr | ASTM D1693B |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C, Compression Molded) | 26.2 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C, Compression Molded) | 1000 | % | ASTM D638 |
| Flexural Modulus - Tangent 1(23°C, 3.18 mm, Compression Molded) | 1240 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength | ASTM D1822 | ||
| -40°C, Compression Molded | 210 | kJ/m² | |
| 23°C, Compression Molded | 252 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 71.1 | °C | ASTM D648 |
| Brittleness Temperature | -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 121 | °C | ASTM D1525 |
| CLTE - Flow | 1.2E-4 | cm/cm/°C | ASTM D696 |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1675 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SABIC® STAMAX 40YM241 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® STAMAX |
| Ultramid® A3EG6 | BASF Corporation | Nylon 66 | Ultramid® |
| POCAN® B 4239 000000 | LANXESS Corporation | PBT | POCAN® |
| LinGen FR345 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TEEE | LinGen |