ProPolymers PAA 5000
| Category: | Nylon Copolymer , Polyamide Copolymer |
| Manufacturer: | ProPolymers Inc. |
| Trademark: | ProPolymers |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HBFY9q_ProPolymersPAA5000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PAA 5000 is a 50% reinforced aromatic nylon copolymer. It has very high stiffness and strength similar to PPA. It can be processed in water heated tools and provides excellent surface finish. It is commonly used in metal and die cast replacement applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.56 | 1.56 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.15 | 0.15 | % | ASTM D955 |
| Transverse flow | 0.95 | 0.95 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.45 | 0.45 | % | ASTM D570 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength (Yield) | 234 | 197 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | |||
| Yield | 3.0 | 4.0 | % | ASTM D638 |
| Fracture | 3.0 | 4.0 | % | ASTM D638 |
| Flexural Modulus | 14500 | 11700 | MPa | ASTM D790 |
| Flexural Strength | 379 | 310 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 130 | 110 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 243 | 243 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 238 | 238 | °C | ASTM D648 |
| Vicat Softening Temperature | 249 | 249 | °C | ASTM D1525 |
| CLTE - Flow | 1.4E-5 | 1.4E-5 | cm/cm/°C | ASTM D696 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-Comp™ PPBGF30-E | Southland Polymers | PP Impact Copolymer | Pro-Comp™ |
| Rynite® 545 BK504 | DuPont Performance Polymers | PET | Rynite® |
| RJM SL701M8M | RJM International, Inc. | PP, Unspecified | RJM |
| Spartech Polycom PP5413 B1 | Spartech Polycom | PP, Unspecified | Spartech |
| 3M™ Dyneon™ PTFE Compound 310192004 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |