Nypel® RC6030F BK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Nypel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HAfKE6_Nypel-RC6030F-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Nypel RC6030F BK is a heat stabilized, 30% glass fiber reinforced, black injection molding grade produced with at least 20% recycled PA6 feedstock. This product is a regional grade available in North America only. Applications Nypel RC6030F BK is generally recommended for applications such as bolts, racks, automotive underhood components, pressure regulator housings and caps. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | |
| Water Absorption | |||
| 24 hr | 1.1 | % | ASTM D570 |
| 23°C, 24 hr | 1.1 | % | ISO 62 |
| Saturation | 6.7 | % | ASTM D570 |
| Saturation, 23°C | 6.7 | % | ISO 62 |
| Equilibrium, 50%RH | 1.9 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.9 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9500 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Break, 23°C | 165 | MPa | ASTM D638 |
| Break, 23°C | 155 | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 8480 | MPa | ASTM D790 |
| 23°C | 8700 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 235 | MPa | ASTM D790 |
| 23°C | 230 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 218 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 203 | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | °C | ASTM D3418, ISO 3146 |
| CLTE | |||
| Flow | 3.8E-5 | cm/cm/°C | ASTM E831 |
| Flow | 2.5E-5 | cm/cm/°C | |
| Transverse | 6.7E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| 1.50 mm | > 1.0E+13 | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Topolymer® M-601J | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| APEX® 3211-85NT | Teknor Apex Company | PVC, Flexible | APEX® |
| FRAGOM PR/420 NAT P | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| Plaskon NXG-1 | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |
| Sylvin 7833-85 Yellow 4203 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |