VYTEEN PC 135
| Category: | PC , Polycarbonate |
| Manufacturer: | Lavergne Group |
| Trademark: | VYTEEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HAD4lL_VYTEEN-PC-135.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vyteen PC 135, Black, medium viscosity polycarbonate, has an excellent balance of stiffness and impact resistance. Features
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 12 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20 mm | 0.50 to 0.70 | % | ASTM D955 |
| 3.20 mm | 0.50 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 60.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2300 | MPa | ASTM D790 |
| -- 3 | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 100 | MPa | ASTM D790 |
| -- 5 | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 700 | J/m | ASTM D256 |
| 23°C | 70 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 120 | °C | ASTM D648, ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 255 to 270 | °C | |
| Middle Temperature | 265 to 280 | °C | |
| Front Temperature | 275 to 295 | °C | |
| Nozzle Temperature | 275 to 295 | °C | |
| Processing (Melt) Temp | 275 to 295 | °C | |
| Mold Temperature | 65.0 to 95.0 | °C | |
| Injection Pressure | 69.0 to 138 | MPa | |
| Injection Rate | Moderate | ||
| Screw Speed | 50 to 75 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax Ultra SC973X | LyondellBasell Industries | PP Impact Copolymer | Pro-fax |
| Ravago Compounds HM-259 | Ravago Manufacturing Americas, LLC | Polyolefin, Unspecified | Ravago Compounds |
| Fainplast PVC PH 55 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Latamid 68 H2-V0 | LATI S.p.A. | Nylon 66/6 | Latamid |
| Kalix® 2855 | Solvay Specialty Polymers | HPPA | Kalix® |