| SUMIKASUPER LCP is a thermotropic liquid crystalline polyester, showing the highest heat resistance among engineering plastics. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.67 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.11 | % | |
| Across Flow | 0.63 | % | |
| Water Absorption (Saturation) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 101 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 134 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.5 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 23°C | 12100 | MPa | |
| 200°C | 4500 | MPa | |
| Flexural Strength | ASTM D790 | ||
| Yield, 23°C | 145 | MPa | |
| Yield, 200°C | 29.0 | MPa | |
| Shear Strength | 53.0 | MPa | ASTM D732 |
| Poisson's Ratio | 0.41 | ASTM E132 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.40 mm) | 120 | J/m | ASTM D256 |
| Unnotched Izod Impact (6.40 mm) | 340 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 270 | °C | ASTM D648 |
| CLTE | Internal Method | ||
| Flow : 150°C | 1.0E-5 | cm/cm/°C | |
| Transverse : 150°C | 6.3E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.56 | W/m/K | JIS R2618 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 4.70 | ||
| 1 MHz | 4.10 | ||
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 0.024 | ||
| 1 MHz | 0.030 | ||
| Arc Resistance | 180 | sec | ASTM D495 |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.300 mm, All colors) | V-0 | UL 94 | |
| Oxygen Index | 45 | % | JIS K7201 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Soldering Resistance | 295 | °C | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 | °C | |
| Drying Time | 4.0 to 24 | hr | |
| Rear Temperature | 280 to 320 | °C | |
| Middle Temperature | 320 to 340 | °C | |
| Front Temperature | 340 to 360 | °C | |
| Nozzle Temperature | 340 to 360 | °C | |
| Processing (Melt) Temp | 340 | °C | |
| Injection Pressure | 80.0 to 160 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 20.0 to 40.0 | MPa | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDP 510 | Marco Polo International, Inc. | HDPE | MARPOL® |
| SUSTAMID 6G LU | Röchling Sustaplast SE & Co. KG | Nylon 6 | SUSTAMID |
| AKROTEK® PEEK GF 50 natural (5100) | AKRO-PLASTIC GmbH | PEEK | AKROTEK® |
| Chemlon® 530 GH | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| EPO-TEK® 310T-M | Epoxy Technology Inc. | Epoxy | EPO-TEK® |